(XYD-Alloy Plastic)可溶性支撑材料HIPS乳白色不透明线材,密度为1.05g/cm^3,熔融温度150~180℃,打印温度230℃-265℃,热分解温度300℃。在常温下溶解于柠檬烯,由于材料的光泽性低表面为亚光,单独打印表面效果外观显得更细腻但综合性能冲击强度较低。配合ABS打印作为支撑材料方便拆除。
PVA水溶性支撑材料,在常温环境下溶于水,无需添加任何溶剂,对人体、环境无毒无害是种环保支撑材料。
材料物理性质 | 检测标准(ASTM) | ABS | 阻燃ABS | HIPS | FLEX | MAX | WOOD | Bamboo | PLA | WOOD | Bamboo | PLA |
比重 Specific Gravity | D792 | 1.05 | 1.17 | 1.05 | 1.2 | 1.27 | 1.05~1.18 | 1.0~1.18 | 1.24 | 1.05~1.18 | 1.0~1.18 | 1.24 |
热变型温度H.D.T Annealed(85℃,8hr) Unannedaled |
1/4",120℃、hr |
99(210) 88(190) |
85(185) 76(169) |
90 | / | 70(0.455Mpa(66psi) | 65 | 65 | 60 | 65 | 65 | 60 |
MFR(200°C,g/10min) | 200℃,5kg | 1.8 | 4.8 | 8 | 12.1 | 20(250℃2.16KG) | 8~18 | 8~18 | 5~12 | 8~18 | 8~18 | 5~12 |
弯曲强度 (MPa)Tensile Strength@Break,psi | ASTM D790 | 820(11660) | 640(kg/c㎡) | D638/450 | / | Mpa(kgf/cm2)71(720) | 5500 | 5500 | 7770 | 5500 | 5500 | 7770 |
拉伸伸长率 Tensile Elongation,% |
ASTM D638 | 20 | 15 | 40 | >400 | 4.5 | 5.5 | 5 | 6 | 5.5 | 5 | 6 |
缺口悬臂梁冲击 Notched lzod lmpact,ft-lb/in(J/m) |
ASTM D256 |
18(3.3) 20(3.7) |
3.8 | 11 | 85 | 85 | 0.06 | 0.06 | 0.1(16) | 0.06 | 0.06 | 0.1(16) |
打印使用温度 Printing temperature |
℃ | 220℃-260℃ | 220℃-260℃ | 210℃-260℃ | 195℃-245℃ | 230℃-260℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ | 190℃-230℃ |